Beryllium

Beryllium,  ₄Be

Ki-pún sèng-chit
Miâ, hû-hō	beryllium, Be
Gōa-hêng	white-gray metallic
Beryllium tī chiu-kî-piáu lāi ê ūi-tì
– ↑ Be ↓ Mg lî-sò͘ ← beryllium → phêng-sò͘
Goân-chú-hoan	4
Goân-chú-liōng (±)	9.0121831(5)
Goân-sò͘ lūi-pia̍t	kiⁿ-thó͘ kim-sio̍k
Cho̍k, hun-khu	2·2·s
Chiu-kî	tē 2 chiu-kî
Tiān-chú pâi-lia̍t	[He] 2s2
per shell	2, 2
Bu̍t-lí sèng-chit
Siòng	kò͘-thé
Iûⁿ-tiám	1560 K ​(1287 °C, ​2349 °F)
Hut-tiám	2742 K ​(2469 °C, ​4476 °F)
Bi̍t-tō͘  (sek-un)	1.85 g·cm−3
1.690 g·cm−3
Lîm-kài-tiám	5205 K,  MPa (extrapolated)
Iûⁿ-hoà-jia̍t	12.2 kJ·mol−1
Cheng-hoat-jia̍t	292 kJ·mol−1
Jia̍t-iông-liōng	16.443 J·mol−1·K−1
cheng-khì-ap P (Pa) 1 10 100 1 k 10 k 100 k tī T (K) 1462 1608 1791 2023 2327 2742
Goân-chú sèng-chit
Sng-hòa-sò͘	+2, +1 ​(an amphoteric oxide)
Tiān-hū-tō͘	Pauling scale: 1.57
Tiān-lī-lêng	1st: 899.5 kJ·mol−1 2nd: 1757.1 kJ·mol−1 3rd: 14,848.7 kJ·mol−1 (more)
Goân-chú pòaⁿ-kèng	empirical: 112 pm
Kiōng-kè pòaⁿ-kèng	96±3 pm
Van der Waals pòaⁿ-kèng	153 pm
Cha̍p-lio̍k
Chiⁿ-thé kò͘-chō	​hexagonal close-packed (hcp)
Siaⁿ-sok (sòe kùn-á)	12,890 m·s−1 (at r.t.)
Jia̍t-phòng-tiòng	11.3 µm·m−1·K−1 (at 25 °C)
Jia̍t-thoân-tō-lu̍t	200 W·m−1·K−1
Tiān-chó͘-lu̍t	36 nΩ·m (at 20 °C)
Chû-sèng	diamagnetic
Young hē-sò͘	287 GPa
Shear hē-sò͘	132 GPa
Bulk hē-sò͘	130 GPa
Poisson pí	0.032
Mohs ngē-tō͘	5.5
Vickers ngē-tō͘	1670 MPa
Brinell ngē-tō͘	590–1320 MPa
CAS teng-kì pian-hō	7440-41-7
Le̍k-sú
Hoat-hiān	Louis Nicolas Vauquelin (1797)
Siōng chá hû-lî	Friedrich Wöhler & Antoine Bussy (1828)
Chòe ún-tēng ê tông-ūi-sò͘
Chú bûn-chiong: beryllium ê tông-ūi-sò͘
iso NA half-life DM DE (MeV) DP 7Be trace 53.12 d ε 0.862 7Li γ 0.477 – 9Be 100% 9Be is stable with 5 neutrons 10Be trace 1.36×106 y β− 0.556 10B

Beryllium sī chi̍t-khóan gôan-sò͘ , sio̍k tē-2-cho̍k chham tē-2-chiu-kî.